KEY WORDS

Multiphase Steel, Zinc Coating, Galvannealing, Cupping Test, the Marginal Coefficient of Drag.

ABSTRACT

Subject of presented contribution is process formability parameters evaluation of both  side coated TRIP and HSLA steels in basic state and after its annealing in order to Fe-Zn coating creation. The samples were annealed at 450, 500 and 550°C for 10 and 60 seconds in argon shielding gas. Obtained values are compared with each other in order to determine whether the influence of temperature and duration after annealing changed the original class inclusion on a scale to measure the quality of steel sheets for deep drawing according to the value of limit drawing ratio. Limit drawing ratio was used as a process formability criterion and were reached by modified Swift cupping test. HSLA steel H220PD and TRIP steel RAK40/70 were used as experimental materials.

CITATION INFORMATION

Acta Mechanica Slovaca. Volume 15, Issue 3, Pages 88 – 93, ISSN 1335-2393

DOWNLOAD

  Verification of the Effect of Temperature and Duration of Stamina for Heat Treatment of Zinc Coating on the Formability of Procedural AHSS Steels

REFERENCES

[1] http://www.salzgitterflachsthal.de/en/News/Archiv/2500/dual_Phase_in_feuerveryinkter_Ausfuehrun[cit:10.10.2010]

[2] HUDÁK, J. -TOMAŠ, M.: VPLYV TEPLOTY A DOBY VÝDRŽE PRI ŽÍHANÍ Zn POVLAKU NA MATERIÁLOVÚ TVÁRNITEĽNOSŤ AHSS OCELÍ. In: Transfér inovácií. Košice: SjF TU, č.15 2009 str. 128-131
[3] JANKURA, D.- BREZINOVÁ, J.: Technické materiály Laboratórne cvičenia, Košice 2006 ISBN 80-8073-412-7
[4] ČAJKOVÁ, L. – DŽUPON, M. – JAKUBÉCZYOVÁ, D.: Spôsob prípravy Fe-Zn povlakov na žiarovo pozinkovaných oceľových plechoch. Acta Mechanica Slovaca, roč. 12, č.4-B/2008, s. 40-45, ISSN 1335-2393
[5] KOLLÁROVÁ, M.- DŽUPON,- LEŠKO, A. –PARILÁK, Ľ.: Formation of Outburst Structure in Hot Dip Galvannealed Coatings on IF Steels METALURGIJA 46 (2007)1,9-14p. 9-14
[6] Džupon, M. -Buríková, K.- Parilák, Ľ.: Methodology of Preparation of Dual Phase Ferrite-Martensitic Steel Micro-Alloyed With V-Nb Manufacturing engineering Issue 1, year VII, 2008, pp. 44-48
[7] ŠVANTNER, P.: Experimentálny výskum lisovateľnosti plechov pre automobilový priemysel s modifikovaným povrchom, Technická Univerzita v Košiciach, 2010.
[8] STN EN 1669 .2001 Skúšobné metódy. Skúška anizotropie plechov a pásov (kalíškovacia)
[9] SPIŠÁK, E. a kol.: Dizajn moderne koncipovaných ocelí na základe charakteristík lisovateľnosti. APVV-0629-06
[10] POLLÁK, L.- HUDÁK, J.- POLLÁKOVÁ, G.- HANDŽÁK, M.:Štúdium procesov plastického pretvorenia pri hlbokom ťahaní. Grantový vedecký projekt č.1/334/94 Košice 1994-5

Latest Issue

ams 2 2016

Download

Guests Online

We have 12 guests and no members online